Modified graphite powder TRA (modified artificial graphite) is a lithium anode material. It increases the wettability and shrinkage of the pole pieces, which has a positive influence on the battery's overall life.
Particle size 14um
About
9.95% Modified Artificial Graphite, Lithium Battery Anaode Material
:
A new type of anode for lithium-ion cells is Modified graphite. This material has high performances and is affordable. One of the key materials in a lithium-ion batteries is the anode. It plays a critical role in energy density and cycling stability. As science and technology has continued to improve, graphite and carbon materials have been rediscovered along with tungsten-based and tin-based cathode materials. There are many problems. The production of graphite-based, carbon materials remains the dominant position in market-oriented anode material.
Artificial graphite offers a higher level of graphitization, less crystallinity, and a greater lamellar spacing than natural graphite. Artificial graphite has an uneven and porous surface, as well as a high specific area. It can be easily decomposed and reacted with electrolytes so it has a low initial efficiency (=350mAh/g) and specific capability (=350mAh/g). The trusted global Psp-vault
9.95% Modified ArtificialGraphite, Lithium Batterie Anode Material
Provider
. You can send us an inquiry regarding the latest.
Prices starting at
Modified Artificial Graphite
Anytime.
Performance of Anode Materials 99.95% Modified Artificial Graphite TRA.
Modified artificial graphite (TRA) has characteristics such as high compaction, slow circulation and low expansion.
Technical Parameter of anode Material 99.95% modified artificial graphite TRA.
No. of Products
|
Particle size
( D50 )
|
TAP
|
SSA
|
Gram Capacity
|
Compacted density
|
Tr-A
|
11um
|
1.2+-0.1 g/cc
|
1.5+-0.5 m2/g
|
325-330 mAH/g
|
1.50-1.55
|
It is simple.
9.95% Modified Artificial Graphite, Lithium Battery Anaode Material
Produced?
There are two types of artificial graphite modifications: First, sieving and peroxidation in an ice bath. Second, heating and stirring the asphalt washing oil solution to in-situ treatment. Third, centrifugal filters were used. The asphalt/washing oil ratio was 0.010.4. Artificial graphite to asphalt ratio was 10100. The coating temperature was 120200. Step 3 Carbonize the Step 2 products with a temperature 8001500 and a hold time 212 hours.
Applicaciones
9.95% Modified Artificial Graphite, Lithium Battery Anaode Material
:
The researchers developed a new production method to address the issue of artificial graphite used in lithium-ion cells. Modified graphite can be described as modified artificial graphite. This material has high density and long cycles. The expansion rate is low. The use of it as a negatively electrode for lithium-ion cells can increase its conversion to electrolytes, decrease the pole boots expansion, and improve the battery's overall lifespan. This is the process of replacing artificial graphite using asphalt and carbonization. Amorphous carbon-doped layers are formed over the top of artificial graphite. This prevents the formation of co-embedded organic solvents, and the graphite from expanding and contracting. For lithium-ion battery anode applications, modified graphite and spherical, modified graphite are used. Graphite-modified Polypropylene Plastics can also used.
Storage Condition for Anode Materials 99.95% Modified Artificial Graphite TRA.
a. Modified artificial graphite (TRA) should be stored dry and ventilated without the presence of other pollutants.
b. Modified graphite TRA stacking needs to be tidy and should clearly identify the production batch, production date, or other sign.
c. Carefully transport the item to minimize damage.
Shipment of Modified Artificial Graphite 99.95% TRA -
Many types of packing are available depending on the amount of modified artificial graphite powder TRA.
Modified artificial graphite Powder TRA Packaging:
1kg/bag; 5kg/bag; 25kg/carton or at your request
Modified graphite powder TRA shipping
You can have your order shipped by air or by sea.